Hishiko operates Magnet Applied Equipment division (formerly known as Fuji Jikoh Co. Ltd.)&Special Welding Consumables division.

Low hydrogen type covered electrode, hardness HRC55～60, less uneven hardness due to high alloy core wire. Composition of deposited metal is even. Excellent performance as antiwear and heat resistant overlaying. Most salable item for edge preparation and overlay-repairing on mould in automobile industry.

Low hydrogen type covered electrode designed for welding SKD11 or similar product and shows high antiwear from low to high temperature.The deposited metal consists of martensite composition as the base and various carbides and has excellent anti-crack performance.

This covered electrode is low hydrogen type and  is suitable for hardfacing on automobile cold mould(HMD-5 、ICD-5、SX105V, etc). and the hardness of deposited metal is HRC50 after welding and about HRC60 after quenching. High welding activity and anti-crack performance.

MH-61S is MAG solid wire, which is most suitable for edge preparation of molds.
The deposited metal gives hardness of HRC53~58 with excellent resistance to heat, impact and wear.

Most suitable solid wire for edge preparation on mould.The hardness of deposited metal is HRC55～58 and usable combined with EA600W.

MH-5S is solid wire for MAG welding which is equivalent to aforementioned MH-5. The performance is equal to MH-5.Less fume compared with flux cored wire and good welding activity and bead appearance.